Anyone had a solid polymer capacitor fail for whatever reason?
How do they fail? Do they explode, go open, short out, ?
How about for different reasons: forcing excessive ripple current, overheating, voltage too high, reverse voltage?
Just wondering about the causes for a potential shorted solid polymer capacitor... trying to debug a board that has a ~4Ω "short" on a track... it may or may not be a capacitor but was wondering what if it were...
How do they fail? Do they explode, go open, short out, ?
How about for different reasons: forcing excessive ripple current, overheating, voltage too high, reverse voltage?
Just wondering about the causes for a potential shorted solid polymer capacitor... trying to debug a board that has a ~4Ω "short" on a track... it may or may not be a capacitor but was wondering what if it were...
Comment